回流法制备纳微棒簇氧化锌的结构与光催化性能
耿涛,吴勇
(宿州学院化学化工学院,宿州学院化学化工学院)
Synthesis and Photocatalytic activity of nano-micro ZnO rod clubclusters by reflux method
geng tao and wu yong
(School of Chemistry & Chemical Engineering, Suzhou Uniersity,School of Chemistry & Chemical Engineering, Suzhou Uniersity)
摘要
图/表
参考文献
相似文献
本文已被:浏览 734次   下载 51
投稿时间:2015-11-05    修订日期:2016-08-24
中文摘要: 采用回流法,以Zn(CH3COO)2?2H2O和氨水为原料,在不额外添加任何分散剂条件下,制备了纳微结构的ZnO棒簇。利用SEM、XRD和EDS等手段对产品的形貌和结构进行了表征。并研究了所制ZnO棒簇降解有机物亚甲基蓝的光催化性能。实验结果表明,所制纳微结构ZnO棒簇,采用可见光照射时间为180min后,对亚甲基蓝的降解率可达96.7%。
中文关键词: ZnO  回流法  亚甲基蓝  光催化性能
Abstract:Nano-micro ZnO rod clubclusters was prepared via reflux method by Zn(CH3COO)2?2H2O and NH3?H2O as raw materials, without using any surfactants. The products were characterized by SEM、XRD and EDS. Photocatalyst of methylene blue (MB), in aqueous solution was investigated by using nano-micro ZnO rod clubclusters as photocatalyst. The results showed that after 180 minutes under visible-light irradiation, the degradation rate of methylene blue was 96.7%.
文章编号:     中图分类号:    文献标志码:
基金项目:
引用文本:
耿涛,吴勇.回流法制备纳微棒簇氧化锌的结构与光催化性能[J].有色金属工程,2016,6(5):.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299224

杂志信息

期刊简介

相关下载

联系我们

电话:86-10-63299224/63299153

传真:010-63299754

Email:ysjsgc@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼

关注微信公众号