航空用7055铝合金微观组织演变及时效处理对性能的影响
李辉,李铸铁,张涛,史春丽,祝贞凤,尹登峰
(烟台南山学院 工学院材料系,山东南山铝业股份有限公司 国家铝合金压力加工工程技术研究中心;山东南山铝业股份有限公司 国家铝合金压力加工工程技术研究中心,烟台南山学院 工学院材料系,山东南山铝业股份有限公司 国家铝合金压力加工工程技术研究中心,烟台南山学院 工学院材料系,中南大学 材料科学与工程学院;中南大学 材料科学与工程学院)
Microstructure evolution and influence of aging treatment on mechanical properties of 7055 aluminum alloy
LiHui,Li Zhu-tie,Zhang Tao,Shi Chun-li,Zhu Zhen-feng and Yin Deng-feng
(YanTai Nanshan University,National engineering research center for plastic working of aluminum alloys,Yantai Nanshan University,National engineering research center for plastic working of aluminum alloys,Yantai Nanshan University,Central South University)
摘要
图/表
参考文献
相似文献
本文已被:浏览 299次   下载 3
投稿时间:2017-03-15    修订日期:2017-03-28
中文摘要: Al-Zn-Mg-Cu系7055铝合金,属航空用高强铝合金,固溶处理后的人工时效过程决定了其微观结构演变及力学性能。本文对不同时效制度下7055铝合金微观组织演变及强度变化规律进行研究,运用金相显微镜、透射电镜观察了微观组织,测试了力学性能。实验结果表明:时效温度为120 ℃时,屈服强度和抗拉强度均呈现单调增加的趋势,并且初期升高速率极快,后续变得平缓,40 h后达到峰值强度;时效温度为160 ℃时,屈服强度与抗拉强度首先急剧升高,10 h后达到峰值强度,随后均呈现明显的降低趋势;人工时效初期,首先生成与基体完全共格的原子团簇及GP区,随后晶内出现过渡η’,直至演变为过时效状态下的平衡η相。
Abstract:Al-Zn-Mg-Cu series 7055 aluminum alloy has high strength,and its microstructure and mechanical properties are determined by the artificial aging process after solution treatment. The evolution of fine structure and mechanical properties of 7055 aluminum alloy at different artificial aging process were investigated in this paper. The microstructure was studied by optical metallurgical microscope(OM) and transmission electron microscope(TEM). The mechanical properties were tested. The results indicate that the yield strength and tensile strength show a increasing trend at 120 ℃,and the increasing speed is high at first and then becomes slowly. The peak value of strength is reached when holding for 40 h at 120 ℃,while only needs 10 h at 160 ℃ and then has a decreasing trend. In microscopic view,the clusters and GP zones are formed during the initial aging process,then the metal-stable η’ is formed,and finally the equilibrium η phase is retained.
文章编号:     中图分类号:    文献标志码:
基金项目:山东省自然科学基金 (ZR2016EMQ11) ,国家十三五重点专项(2016YFB0300802)
引用文本:
李辉,李铸铁,张涛,史春丽,祝贞凤,尹登峰.航空用7055铝合金微观组织演变及时效处理对性能的影响[J].有色金属工程,2018,8(3):.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299224

杂志信息

期刊简介

相关下载

联系我们

电话:86-10-63299224/63299153

传真:010-63299754

QQ:XXXXXXX

Email:ysjsgc@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼

关注微信公众号