钛基Ce掺杂SnO2-RuO2电极的制备及其对焦化废水的电解处理
(1.内蒙古科技大学;2.中冶西北工程技术有限公司)
Preparation of Ti-Based Ce-Doped SnO2-RuO2 Electrode and Its Electrolytic Treatment of Coking Wastewater
wangweida1, haowenting1, wangjianguo1, liuyijie2, zhangyan3,4,5, liweiping3,4,5
(1.Inner Mongolia University of Science&Technology;2.MCC Northwest Engineering Technology Co., Ltd.;3.Inner Mongolia University of Science&4.amp;5.Technology)
摘要
图/表
参考文献
相似文献
本文已被:浏览 45次   下载 26
投稿时间:2019-04-22    修订日期:2019-05-09
中文摘要: 采用溶胶-凝胶法制备了经稀土元素Ce掺杂改性的Ti/RuO2-SnO2-Ce电极,利用SEM、XRD、EDS等分析方法对电极表面的形貌、物相和涂层成分进行了表征,利用CV曲线、LSV曲线等检测手段对电极的电化学性能进行了测试。以Ti/RuO2-SnO2-Ce电极为阳极,钛板为阴极,构建电化学氧化反应装置,并采用其对焦化废水进行电解处理。结果表明,Ti/RuO2-SnO2电极经稀土Ce改性后极板表面活性位点数量明显增大,金属涂层的结晶化程度明显增强,电极的催化氧化活性显著提高。室温条件下,保持pH值为7.83,在电流密度为30 mA/cm2,电解时间为30 min,焦化废水经电解处理后COD去除率可达91.63%,TOC去除率可达66.22%,UV254值下降到0.921。
Abstract:The Ti/RuO2-SnO2-Ce electrode modified by doping with rare earth element Ce was prepared by sol-gel method. The morphology, phase, and coating composition of the electrode surface were characterized by scanning electron microscope (SEM), X-ray diffraction (XRD), energy disperse spectroscopy (EDS) and other analytical methods. And the electrochemical performance of the electrode was tested using detection methods such as CV curve and LSV curve. Taking Ti/RuO2-SnO2-Ce electrode as the anode and a titanium plate as the cathode, an electrochemical oxidation reactor was constructed and used for electrolytic treatment of coking wastewater. The results show that the number of active sites on the surface of Ti/RuO2-SnO2 electrode modified by rare earth Ce increased significantly, the crystallization of the metal coating was obviously enhanced, and the catalytic oxidation activity of the electrode was remarkably improved. At room temperature, the pH was maintained at 7.83, the current density was 30 mA/cm2, and the electrolysis time was 30 min. After the electrolytic treatment of coking wastewater, the COD removal rate and the TOC removal rate reached 91.63% and 66.22%, respectively, and the UV254 value decreased to 0.921.
文章编号:     中图分类号:X703.1    文献标志码:
基金项目:内蒙古自然科学基金资助项目(2018LH04003);包头科技计划重点领域技术攻关项目(2017Z1009-1);内蒙古科技大学创新基金资助项目(2016QDL-B08);内蒙古自然科学基金博士基金资助项目(2016BS0511)
引用文本:
王维大,郝文亭,王建国,刘奕杰,张妍,李卫平.钛基Ce掺杂SnO2-RuO2电极的制备及其对焦化废水的电解处理[J].有色金属工程,2020,(2):29-35.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299224

杂志信息

期刊简介

相关下载

联系我们

电话:86-10-63299224/63299153

传真:010-63299754

QQ:XXXXXXX

Email:ysjsgc@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼

关注微信公众号